EN 1.7131 Steel 16MnCr5 Material Equivalent, Composition, Properties


EN 1.7131 Steel 16MnCr5 Material现货价格查询

EN 1.7131 steel (16MnCr5 material) is an European standard carburized steel (case hardening steel) with good hardenability and machinability. For larger cross-section parts, high surface hardness and wear resistance can be obtained after heat treatment, and low-temperature impact toughness is also high. For specification and datasheet, please see the tables below.

16MnCr5 steel is generally used after carburizing and quenching, and is mainly used for manufacturing gears, worms, sealing bushings and other components.

Datasheet

The following tables show material 16MnCr5 datasheet and specification including chemical composition, mechanical properties, etc.

(DIN EN 1.7131 Material) 16MnCr5 Steel Chemical Composition

The following table shows chemical composition of 16MnCr5 material (1.7131 steel).

    Chemical Composition %
Standard Steel Name (Steel Number) C Si ≤ Mn P ≤ S Cr
EN 10084 16MnCr5 (1.7131) 0.14-0.19 0.40 1.00-1.30 0.025  ≤ 0.035 0.80-1.10
EN 10084 16MnCrS5 (1.7139) 0.14-0.19 0.40 1.00-1.30 0.025 0.020-0.040 0.80-1.10

Mechanical Properties of 1.7131 Steel (16MnCr5 Material)

1.7131 material, 16MnCr5 steel Brinell hardness

  • Soft annealed: ≤ 207 HBW
  • Treated to hardness: 156-207 HBW
  • Treated to ferrite-pearlite structure and hardness: 140-187 HBW
  • Normalized: 138-187 HBW

EN 1.7131, 16MnCr5 Tensile strength (after hardening and tempering at 200 °C)

  • Dia. ≤ 16mm: Min. 1000 MPa
  • 16 < Dia. ≤ 40mm: Min. 800 Mpa
  • 40 < Dia. ≤ 100mm: Min. 600 Mpa

Heat Treatment Specification of 16MnCr5 (1.7131 Steel)

  • End quench test Austenitizing temperature: 870℃ (30-35 minutes)
  • Carburizing temperature: 880-980 ℃
  • Core-hardening temperature: 860-900 ℃
  • Case-hardening temperature: 780-820 ℃
  • Tempering: 150 – 200 ℃ (≥ 1 hour)

Equivalent Grade

EN 1.7131 material (16MnCr5 steel) equivalent to ISO, US ASTM AISI SAE, Japanese JIS and Chinese GB standard.(For reference)

16MnCr5 steel equivalent
European ISO USA Japan China
Standard Grade (Steel Number) Standard Grade Standard Grade (a) Standard Grade (b) Standard Grade
EN 10084 16MnCr5 (1.7131) ISO 683-11 16MnCr5 AISI SAE;
ASTM A29/A29M
5115 JIS G4053 SCr415 GB/T 5216 16CrMnH